Magnolia 6168 A/B
Description
Magnolia 6168 A/B is a two-part epoxy having good peel strength and high temperature properties.
Properties
Property
|
Magnolia 6168 A/B
|
|
|
Cure Schedule
|
Set – 6-12 hours @ 75°F; Full Cure – 7 days @ 75°F
|
Mix Ratio – Parts By Weight (Part A:Part B)
Parts By Volume (Part A:Part B)
|
100:44
2:1
|
Pot Life, 3 ounces
|
45 minutes
|
Shelf Life
|
A: 6 months B: 6 months @ 75°F
|
Specific Gravity
|
Part A: 1.1
Part B: 1.0
Mix: 1.1
|
Viscosity @ 77°F
|
Part A: Semi-Paste
Part B: Paste
Mix: Paste
|
SPI Classification
|
A: 4 B: 4
|
Flash Point
|
A: >200°F B: >200°F
|
Flammable Under 100°F
|
A: No B: No
|
Combustible 100-200°F
|
A: No B: No
|
Corrosive
|
A: No B: Yes
|
Freight Class
|
A: 1 B: 2
|
Properties After 7 Day Cure @ 75°F
Property
|
Magnolia 6168 A/B
|
|
|
Lap Shear Strength, ASTM D-1002, Room Temperature Test
|
4000 psi (27.58 N/mm2)
|
Lap Shear Strength, ASTM D-1002, -67°F Test After 10 Minute Exposure
|
4000 psi (27.58 N/mm2)
|
Lap Shear Strength, ASTM D-1002, 180°F Test after 10 minute exposure
|
2500 psi (17.24 N/mm2)
|
Lap Shear Strength, ASTM D-1002, 250°F Test after 10 minute exposure
|
1500 psi (10.34 N/mm2)
|
T-Peel, ASTM D-1876, 0.012 inch bond line
|
45 piw (198 N/25mm
|
Glass Transition Temperature, tested using DSC
|
102°C
|
Hardness, Shore “D”
|
75-80
|
Note: Adhesion tested on FPL etched 2024 T-3 Aluminum.
DANGER
|
FIRST-AID
|
-
May cause severe irritation.
-
Do not get in eyes, on skin or clothing.
-
Do not inhale vapors.
-
Wear rubber gloves & aprons.
-
Use with adequate ventilation.
-
Wash thoroughly after handling.
|
-
Eyes - Immediately flush eyes with plenty of water for at least 15 minutes. Get medical attention.
-
Skin - Wash immediately with soap and water.
-
Clothing - Remove clothing and wash before reuse.
|
For Industrial Use ONLY. Keep container closed. Do Not Reuse this Container.
|
The information on this sheet is based upon data obtained by our own research and is considered accurate. However, no warranty is expressed or implied regarding the results to be obtained from the use of this data or that any such use will not infringe on any patent. This information is furnished upon the condition that the person receiving it shall make his own tests to determine the suitability thereof for this particular purpose.